| HIPS PH-888H 镇江奇美有限公司 物性数据 |
①原料描述部分
| 规格级别： |
--- |
外观颜色： |
--- |
| 用途概述： |
--- |
| 备注说明： |
耐热高抗冲击 |
②原料技术数据
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
溶体流动速率 |
200℃,5kg |
ASTM D-1238 |
3.6 |
g/10min |
| 溶体流动速率 |
200℃,10kg |
ISO-1133 |
32 |
g/10min |
| 物理性能 |
比重 |
--- |
ASTM D-792 |
1.05 |
--- |
| 机械性能 |
引张强度 |
--- |
ASTM D-638 |
300 |
kg/cm2 |
| 延伸率 |
--- |
ASTM D-638 |
70 |
% |
| 弯曲弹性率 |
--- |
ASTM D-790 |
2.0 |
104kg/cm2 |
| 弯曲强度 |
--- |
ASTM D-790 |
440 |
kg/cm2 |
| 洛氏硬度 |
--- |
ASTM D-785 |
L-85 |
--- |
| IZOD缺口冲击强度 |
1/8" |
ASTM D-256 |
11.0 |
Kg-cm/cm |
| IZOD缺口冲击强度 |
1/4" |
ASTM D-256 |
8.0 |
Kg-cm/cm |
| 热 性 能 |
维卡软化点 |
--- |
ASTM D-1525 |
102 |
°C |
| 热变形温度 |
--- |
ASTM D-648 |
95 |
°C |
| 燃烧率 |
--- |
UL-94 |
HB |
--- | |
| |
|